For electroplating,$1.5 \ A$ current is passed for $250 \ s$ through $250 \ mL$ of $0.15 \ M$ solution of $MSO_4$. Only $85 \ \%$ of the current was utilised for electrolysis. The molarity of $MSO_4$ solution after electrolysis is closest to $.......$ [Assume that the volume of the solution remained constant] (in $M$)

$A$ metal surface of $100 \, cm^2$ area has to be coated with a nickel layer of thickness $0.001 \, mm$. $A$ current of $2 \, A$ was passed through a solution of $Ni(NO_3)_2$ for '$x$' seconds to coat the desired layer. The value of $x$ is $.........$. (Nearest integer)
($\rho_{Ni}$ (density of Nickel) is $10 \, g \cdot cm^{-3}$,Molar mass of Nickel is $60 \, g \cdot mol^{-1}$,$F = 96500 \, C \cdot mol^{-1}$)

$A$ current of $2 \ A$ passing for $5 \ hours$ through molten tin salt deposited $22.2 \ g$ of tin. The oxidation state of tin in the salt is . . . . . . . (Atomic mass of $Sn = 119$)

The relation between Faraday constant $(F)$,chemical equivalent $(E)$,and electrochemical equivalent $(Z)$ is

When a current of $0.6 \ A$ is passed through an aqueous solution of $CuSO_4$ for $7 \ minutes$,what is the total quantity of electricity passed in Faradays?

How many electrons would be required to deposit $6.35 \ g$ of copper at the cathode during the electrolysis of an aqueous solution of copper sulphate? (Atomic mass of copper $= 63.5 \ u$,$N_A =$ Avogadro's constant)